Soft, aliphatic, water-borne polyurethane dispersion in a blend of DMM and propylene glycol solvents.

Suggested Uses: L-2985 was designed for use in textile applications that require a soft hand coupled with very good strength, abrasion resistance, excellent adhesion, and excellent resiliency. Due to its overall properties, L-2985 can be used as a finish or a coating. This versatile urethane is ideally suited for use as a finish for nylon and polyester threads and as a coating for nylon and vinyl substrates. L-2985 is also ideally suited for textile-coating applications that require excellent low temperature flex crack resistance. The low melt temperature also allows L-2985 to be used as a heat seal coating. When properly formulated, L-2985 can be used as a coating for awning fabrics, boat cover fabrics, and other architectural fabrics.

  • NMP-free, APEO-free
  • Superior flexibility
  • Soft, tough, flexible film
  • Good abrasion resistance
  • Superior low temperature, flex-crack resistance
  • Low melting point (265 ºF)
Unit of Measure

Physical Properties


N/A 35 %

Solids Tolerance

N/A ± 1 %


N/A 50 to 500 cps


N/A 7.5 to 10.0


N/A 8.9 lb/gal

Softening Point

N/A 265 ºF

Volatile Organic Compounds (VOC) Content (As Supplied)

N/A 129 g/L

Tensile Properties


N/A 550 %

Tensile Strength

N/A 4000 psi

100 % Modulus

N/A 500 psi

200 % Modulus

N/A 900 psi

300 % Modulus

N/A 1500 psi


N/A Tested at 20 inches/minute


N/A L-2985 may be used as a sole vehicle or blended with acrylic emulsions. Viscosity modification can be made with associative thickeners for application by spray, knife-over-roll, or other methods.


N/A Typical oven drying temperatures and dwell times for aqueous coatings are sufficient to produce optimal film properties. Do not use crosslinking agents for heat-seal coating applications.