Solids |
N/A 35 % |
Solids Tolerance |
N/A ± 1 % |
Viscosity |
N/A 50 to 300 cps |
pH |
N/A 8.5 to 10.0 |
Density |
N/A 8.7 lb/gal |
Softening Point |
N/A 335 ºF |
Volatile Organic Compounds (VOC) Content (As Supplied) |
N/A 67 g/L |
Note for Physical Properties |
N/A Provisional - Physical properties are considered provisional until at least 10 production batches have been produced. |
Elongation |
N/A 210 % |
Tensile Strength |
N/A 6800 psi |
100 % Modulus |
N/A 4900 psi |
200 % Modulus |
N/A 6750 psi |
Note for Tensile Properties |
N/A
Films are coalesced with 5 % DPM to ensure optimal film formation. Tested at 20 Inches/Minute |
N/A L-2877 can be used as a sole vehicle or blended with acrylic emulsions for spray or rotogravure applications. Rheology modifications can be made with associative thickeners for alternative application methods. |
N/A The addition of coalescing solvent is recommended to achieve optimal film formation with L-2877. In ambient-cured systems the addition of 5 - 10 % DPnB coalescing solvent is suggested. Less coalescing solvent is required in heat-cured systems to attain comparable film properties. Typical drying temperatures and dwell times for aqueous coatings are sufficient to produce optimal film properties. |