A hard, co-solvent free, aliphatic, polyester polyurethane dispersion.
Unit of Measure

Physical Properties

Solids

N/A 35 %

Solids Tolerance

N/A ± 1 %

Viscosity

N/A 50 to 500 cps

pH

N/A 7.5 to 10.0

Density

N/A 8.8 lb/gal

Softening Point

N/A 360 ºF

Volatile Organic Compounds (VOC) Content (Less Water)

N/A 45 g/L

Tensile Properties

Elongation

N/A 260 %

Tensile Strength

N/A >6000 psi

100 % Modulus

N/A 4300 psi

200 % Modulus

N/A 5500 psi

Note for Tensile Properties

N/A Tested at 20 Inches/Minute

Suggested Uses

N/A L-3615 was designed for topcoat applications on a wide variety of substrates, including concrete, metal, plastic and wood. It may also be used as a blending resin with the softer L-3614 to impart greater film flexibility. A balanced composition provides good stability with acrylics and confers superior strength, abrasion resistance and low temperature flexibility properties.

Characteristics

N/A

  • Co-solvent free, TEA free, Tin free, APEO free
  • Medium hard, tough, dry film
  • Excellent water and chemical resistance
  • Superior abrasion resistance
  • Good adhesion to a wide variety of substrates

Application

N/A L-3615 can be used as a sole vehicle or blended with other coatings for spray or pad bath applications. Solids can be adjusted with water to optimize dry coating weight. This product may also be thickened with associative thickeners for knife-over-roll or similar methods.

Curing

N/A L-3615 can be air dried, if desired, depending on film thickness. Typical drying temperatures and dwell times for aqueous coatings are sufficient to produce optimal film properties.