Solids |
N/A 38 % |
Solids Tolerance |
N/A ± 1 % |
Viscosity |
N/A 50 to 500 cps |
pH |
N/A 7.0 to 9.5 |
Density |
N/A 8.7 lb/gal |
Softening Point |
N/A 345 ºF |
Volatile Organic Compounds (VOC) Content (As Supplied) |
N/A 30 g/L |
Sward Hardness |
N/A 46 |
Elongation |
N/A 190 % |
Tensile Strength |
N/A >5900 psi |
100 % Modulus |
N/A 4400 psi |
Note |
N/A Tested at 2 Inches/Minute |
N/A L-2875 can be used as supplied or blended with acrylic emulsions for spray, dip or rotogravure applications. It can be thickened with associative thickeners for knife-over-roll or similar methods. |
N/A Due to the co-solvent free nature of L-2875, the addition of coalescing solvent is recommended to achieve optimal film formation. In ambient-cured systems the addition of 5 - 10 % coalescing solvent is suggested. Less coalescing solvent is required in heat-cured systems to attain comparable film properties. Typical drying temperatures and dwell times for aqueous coatings are sufficient to optimize film characteristics |