An aliphatic, silicone-modified, polyester-based, water-borne polyurethane dispersion.

Suggested Uses: L-3466 was designed primarily for topcoat applications where slip and abrasion resistance properties are required. L-3466 contains a non-fugitive silicone component that provides low surface tension characteristics on flexible and rigid substrates including leather, plastics, metals and textiles. It also demonstrates exceptional dye transfer resistance in automotive leather seating and dry-erase, white board applications when crosslinked.

Characteristics:
  • May be formulated into low surface tension coatings
  • Exceptional dye transfer resistance
  • Excellent abrasion resistance
  • Higher silicone content (~2X) than HD-2602
  • Crosslinkable for improved adhesion and performance
  • Contains n-ethyl pyrrolidone (NEP) co-solvent
Unit of Measure

Physical Properties

Solids

N/A 35 %

Solids Tolerance

N/A ± 1 %

Viscosity

N/A 50 to 500 cps

pH

N/A 7.0 to 9.5

Density

N/A 8.7 lb/gal

Softening Point

N/A 305 ºF

Volatile Organic Compounds (VOC) Content (As Supplied)

N/A 99 g/L

Volatile Organic Compounds (VOC) Content (Less Water)

N/A 238 g/L

Sward Hardness

N/A 35

Tensile Properties

Elongation

N/A 300 %

Tensile Strength

N/A >6000 psi

100 % Modulus

N/A 3000 psi

200 % Modulus

N/A 4500 psi

Note for Tensile Properties

N/A Tested at 20 Inches/Minute

Application

N/A L-3466 may be used as a sole vehicle or blended with acrylic emulsions for spray or rotogravure applications. Rheology modifications can be made with associative thickeners for alternative application methods.

Drying

N/A L-3466 can be air dried, if desired, depending on film thickness. Typical oven drying temperatures and dwell times for aqueous coatings are sufficient to produce optimal film properties.

Note

N/A Provisional specifications