A self-crosslinking, aliphatic, water-based polyurethane dispersion designed for use in high performance concrete and wood floor coatings.

Suggested Uses: L-3385 employs a unique air-dry, self-crosslinking mechanism to impart chemical-resistance, abrasion-resistance and mar-resistance properties which equal or exceed those of two-component, water-based floor coating systems currently used in the market.

Characteristics:
  • One-component, self-crosslinking polymer
  • High level of toughness, abrasion- and mar-resistance
  • Outstanding water and chemical resistance
  • Excellent exterior weathering performance
  • Contains n-ethyl pyrrolidone (NEP) co-solvent
Unit of Measure

Physical Properties

Solids

N/A 32 %

Solids Tolerance

N/A ± 1 %

Viscosity

N/A 50 to 300 cps

pH

N/A 7.0 to 10.0

Density

N/A 8.8 lb/gal

Volatile Organic Compounds (VOC) Content (Less Water)

N/A 246 g/L

Note for Physical Properties

N/A Provisional - Physical properties are considered provisional until at least 10 production batches have been produced.

Tensile Properties

Elongation

N/A 160 %

Tensile Strength

N/A 2400 psi

100 % Modulus

N/A 1850 psi

Note for Tensile Properties

N/A Films are coalesced with 5 % DPM to ensure optimal film formation.
Tested at 20 Inches/Minute

Application

N/A L-3385 can be used as a sole vehicle or blended with acrylic emulsions for spray or rotogravure applications. Rheology modifications can be made with associative thickeners for alternative application methods.

Drying

N/A Ambient drying temperatures between 60 - 90 ºF are ideal to produce coatings with optimal film properties. Allow 5 - 7 days to attain full cure properties.