A medium soft, high solids, co-solvent free, aliphatic, polyurethane dispersion.

Suggested Uses: HD-4664 was designed as a high solids, multi-purpose textile binder polymer. It may be used as a blending resin for harder polyurethane polymers to impart greater film flexibility. A balanced composition provides good stability with acrylic latices and confers superior strength, abrasion resistance and low temperature flexibility properties.

Characteristics:
  • High solids (50 %)
  • Contains no co-solvent
  • Medium soft, tough, dry film
  • Superior abrasion resistance
  • Exceptional low temperature flexibility and crack resistance
Unit of Measure

Physical Properties

Solids

 N/A 50 %

Solids Tolerance

 N/A ± 1 %

Viscosity

 N/A 200 to 800 cps

pH

 N/A 7.5 to 10.0

Density

 N/A 8.8 lb/gal

Softening Point

 N/A 310 ºF

Volatile Organic Compounds (VOC) Content (As Supplied)

 N/A 12 g/L

Sward Hardness

 N/A 14

Tensile Properties

Elongation

 N/A 625 %

Tensile Strength

 N/A >6000 psi

100 % Modulus

 N/A 800 psi

200 % Modulus

 N/A 1100 psi

300 % Modulus

 N/A 1500 psi

Note

 N/A Tested at 20 Inches/Minute

Application

N/A HD-4664 can be used as a sole vehicle or blended with acrylic emulsions for spray or pad bath applications. Solids can be reduced with water to optimize dry coating weight. This product may also be thickened with associative thickeners for knife-over-roll or similar methods.

Curing

N/A HD-4664 can be air dried, if desired, depending on film thickness. Typical drying temperatures and dwell times for aqueous coatings are sufficient to produce optimal film properties.